To better understand the generation of electric power for piezoelectric Pb Zr Ti O3（PZT） ceramic plate（?25 mm）, an attempt was made to investigate experimentally and numerically electricpower generation characteristics during cyclic bending under various loading fixtures（?0–?20 mm）, i.e., different contact areas. Increasing the load-contact area on the PZT ceramic leads to a nonlinear decrease in the generated voltage. Decreasing contact area basically enhances the generated voltage, although the voltage saturates during loading when the contact area is less than ?5 mm. A similar voltage is generated for ?0 and ?5 mm, which is attributed to strain status（ratio of compressive and tensile strain） and material failure due to different stress distribution in the PZT ceramic. On the basis of the obtained electric generation voltage, suitable loading conditions are clarified by loading with the ?5 mm fixture, which generates a higher voltage and a longer lifetime of the PZT ceramic. From this approach, it is appeared that the area contact with the area ratio of 0.04（?5 mm/?20 mm） is suitable to obtain the high efficiency of the electric voltage.
类型: 期刊论文
作者: Mitsuhiro OKAYASU,Tsukasa OGAWA
来源: Journal of Advanced Ceramics 2019年04期
年度: 2019
分类: 工程科技Ⅰ辑,工程科技Ⅱ辑
专业: 电力工业
单位: Graduate School of Natural Science and Technology, Okayama University
分类号: TM282;TM61
页码: 509-518
总页数: 10
文件大小: 1210K
下载量: 17
本文来源: https://www.lunwen90.cn/article/4f966611511ef4d39e12b515.html