Because of the excellent mechanical properties of 34 CrNiMo6 steel, it is widely used in high-value components. Many conventional approaches to strengthening-steels typically involve the loss of useful ductility.In this study, 34 CrNiMo6 Steel having high strength and ductility is produced by laser solid forming（LSF）with a quenching-tempering（QT） treatment. Tempering of bainite is mainly by solid phase transformation in the previous LSF layers during the LSF process. The stable microstructure of LSF consists of ferrite and fine carbides. The microstructure transfers to tempered sorbite after heat-treatment. The tensile properties of the LSF steel meet those of the wrought standard. The UTS and elongation of LSF sample at 858 MPa, 19.2%, respectively, are greater than those of the wrought. The QT treatment enhanced the ultimate tensile strength and yield strength of the LSF sample. The ultimate tensile strength, yield strength, reduction in area, and elongation of the LSF+QT sample at 980 MPa, 916 MPa, 58.9%, and 13.9%,respectively, are greater than those of the wrought standard. The yield strength of the LSF+QT sample is approximately 1.27 times that of the wrought. The LSF samples failed in a ductile fracture mode, while the LSF+QT samples showed mixed-mode failure. The defects have only a small effect on the tensile properties owing to the excellent ductility of the LSF sample.
论文目录
文章来源
类型: 期刊论文
作者: Chunping Huang,Xin Lin,Fencheng Liu,Haiou Yang,Weidong Huang
来源: Journal of Materials Science & Technology 2019年02期
年度: 2019
分类: 工程科技Ⅰ辑
专业: 金属学及金属工艺
单位: State Key Laboratory of Solidification Processing, Northwestern Polytechnical University,Engineering Research Center in Additive Manufacturing, Nanchang Hangkong University
基金: supported by National Natural Science Foundation of China (Grant Nos. 51565041,51465044 and 51323008),the National Key Research and Development Program of China (No. 2016YFB1100100),the fund of the State Key Laboratory of Solidification Processing in NWPU (No. SKLSP201634)
分类号: TG665;TG142.1
页码: 377-387
总页数: 11
文件大小: 2791K
下载量: 28
相关论文文献
- [1].Simultaneously enhanced strength and ductility of 6xxx Al alloys via manipulating meso-scale and nano-scale structures guided with phase equilibrium[J]. Journal of Materials Science & Technology 2020(06)
- [2].Micromechanical simulation on strength and ductility of two kinds of Al-based nanostructural materials[J]. Acta Mechanica Solida Sinica 2017(04)
- [3].High strength and ductility Mg-8Gd-3Y-0.5Zr alloy with bimodal structure and nano-precipitates[J]. Journal of Materials Science & Technology 2020(09)
- [4].Hot ductility of DSS and its microstructure observation during hot deformation[J]. Baosteel Technical Research 2010(S1)
- [5].Effect of structural characteristics distribution on strength demand and ductility reduction factor of MDOF systems considering soil-structure interaction[J]. Earthquake Engineering and Engineering Vibration 2012(02)
- [6].Effects of V and Zr Additions on Microstructures and Mechanical Properties of Nb-Ti-Al-Base Alloys[J]. 稀有金属材料与工程 2009(S3)
- [7].Achieving high strength and high ductility in nanostructured metals: Experiment and modelling[J]. Theoretical & Applied Mechanics Letters 2012(02)
- [8].Tensile ductility improvement of AlSi9Cu1 alloy by chemical composition optimization[J]. China Foundry 2017(02)
- [9].Detwinning-induced reduction in ductility of twinned copper nanowires[J]. Chinese Science Bulletin 2013(06)
- [10].Recent developments of the high strength and high ductility nanostructured materials[J]. Baosteel Technical Research 2010(S1)
- [11].A simultaneous improvement of both strength and ductility by Sn addition in as-extruded Mg-6Al-4Zn alloy[J]. Journal of Materials Science & Technology 2020(14)
- [12].Laminated Fe-34.5 Mn-0.04C composite with high strength and ductility[J]. Journal of Materials Science & Technology 2018(10)
- [13].Effect of rare earth cerium and impurity tin on the hot ductility of a Cr-Mo low alloy steel[J]. Journal of Rare Earths 2016(10)
- [14].The First-principles Study on the Occupation Behavior and the Ductility Mechanism of Zr in Ni-Ni_3Al System with Lattice Misfit[J]. Journal of Materials Science & Technology 2014(05)
- [15].High strength-ductility nano-structured high manganese steel produced by cryogenic asymmetry-rolling[J]. Journal of Materials Science & Technology 2018(04)
- [16].Strategies for improving ductility of ordered intermetallics[J]. Progress in Natural Science:Materials International 2016(01)
- [17].P-Δ effect on inelastic displacement ratio spectra for inelastic structures[J]. Journal of Harbin Institute of Technology 2011(01)
- [18].Hot ductility behavior of V-N and V-Nb microalloyed steels[J]. International Journal of Minerals Metallurgy and Materials 2012(06)
- [19].Effect of foundation flexibility on ductility reduction factors for R/C stack-like structures[J]. Earthquake Engineering and Engineering Vibration 2011(02)
- [20].Toughening FeMn-based high-entropy alloys via retarding phase transformation[J]. Journal of Materials Science & Technology 2020(16)
- [21].Effects of alloy elements on ductility and thermal conductivity of compacted graphite iron[J]. China Foundry 2018(03)
- [22].Effect of 0.5 mass% Cu Addition on Ductility and Magnetic Properties of Fe-6.5Si Alloy[J]. Journal of Iron and Steel Research(International) 2016(07)
- [23].Effects of Stress Level and Stress State on Creep Ductility:Evaluation of Different Models[J]. Journal of Materials Science & Technology 2016(08)
- [24].Effects of Ti-Ce refiners on solidification structure and hot ductility of Fe-36Ni invar alloy[J]. Journal of Rare Earths 2013(09)
- [25].Competing failure mechanisms of thin metal films on polymer substrates under tension[J]. Theoretical & Applied Mechanics Letters 2011(04)
- [26].Hot Ductility of Ti-V Bearing Microalloyed Steel in Continuous Casting[J]. Journal of Iron and Steel Research(International) 2014(04)
- [27].Hot Ductility of DSS and Its Microstructure Observation During Hot Deformation[J]. Journal of Iron and Steel Research(International) 2013(08)
- [28].High-temperature mechanical properties of near-eutectoid steel[J]. International Journal of Minerals Metallurgy and Materials 2013(09)
- [29].First-Principles Prediction of Ductility in β-type Ti-Mo Binary Alloys[J]. Journal of Shanghai Jiaotong University(Science) 2011(02)
- [30].Effect of Zr, Hf, and Sn Additives on Elastic Properties of α_2-Ti_3Al Phase by First-principles Calculations[J]. Journal of Wuhan University of Technology(Materials Science) 2017(04)